| The Sarlink TPV 5700B series are highly engineered extrusion-grade thermoplastic vulcanizates with outstanding UV stability designed for demanding automotive interior and exterior sealing applications, including glass run channels, waistbelts, weather strips, seals and other profiles. Sarlink TPV X5780B is a medium hardness, medium density, high performance grade with low fogging and excellent color retention and elastic properties.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good Dimensional Stability,High Heat Resistance,Elastic,Solvent resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.968 | g/cm³ | ASTM D792 |
| Density | 0.970 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 4.50 | MPa | ASTM D412 |
| MD, 100% strain | 6.80 | MPa | ASTM D412 |
| tensile strength | ISO 37 | ||
| TD, 100% strain | 4.50 | MPa | ISO 37 |
| MD, 100% strain | 6.80 | MPa | ISO 37 |
| tensile strength | ASTM D412 | ||
| fracture | 10.0 | MPa | ASTM D412 |
| MD, fracture | 9.03 | MPa | ASTM D412 |
| tensile strength | ISO 37 | ||
| fracture | 10.0 | MPa | ISO 37 |
| MD, fracture | 9.00 | MPa | ISO 37 |
| Tensile strain | ASTM D412 | ||
| fracture | 590 | % | ASTM D412 |
| Flow rate, fracture | 360 | % | ASTM D412 |
| Tensile strain | ISO 37 | ||
| fracture | 590 | % | ISO 37 |
| Flow rate, fracture | 360 | % | ISO 37 |
| tear strength | |||
| TD | 47 | kN/m | ISO 34-1 |
| TD | 47.3 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395 | ||
| 23℃，22 hr | 28 | % | ASTM D395 |
| 70℃，22 hr | 41 | % | ASTM D395 |
| 125℃，70 hr | 60 | % | ASTM D395 |
| Compression deformation | ISO 815 | ||
| 23℃，22 hr | 28 | % | ISO 815 |
| 70℃，22 hr | 41 | % | ISO 815 |
| 125℃，70 hr | 60 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shore A, 5 seconds, extrusion molding | 80 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 82 | ISO 868 | |
| Shore hardness | ASTM D2240 | ||
| Shore A, 5 seconds, extrusion molding | 80 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 82 | ASTM D2240 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Electrical performance | 50.0 | ℃ | UL 746 |
| Strength mechanical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Change rate of tensile strength in air – TD | ASTM D573 | ||
| 135℃，1000 hr | -10 | % | ASTM D573 |
| 100% strain, 135 ℃, 1000 hr | 10 | % | ASTM D573 |
| 150℃，168 hr | -12 | % | ASTM D573 |
| 100% strain, 150 ℃, 168 hr | 7.0 | % | ASTM D573 |
| Change rate of tensile strength in air – TD | ISO 188 | ||
| 135℃，1000 hr | -10 | % | ISO 188 |
| 100% strain 135 ℃, 1000 hr | 10 | % | ISO 188 |
| 150℃，168 hr | -12 | % | ISO 188 |
| 100% strain 150 ℃, 168 hr | 7.0 | % | ISO 188 |
| Change rate of ultimate elongation in air – TD | ASTM D573 | ||
| 135℃，1000 hr | -19 | % | ASTM D573 |
| 150℃，168 hr | -20 | % | ASTM D573 |
| Changes in tensile stress when fractured in air – TD | ISO 188 | ||
| 135℃，1000 hr | -19 | % | ISO 188 |
| 150℃，168 hr | -20 | % | ISO 188 |
| The rate of change in hardness of a hardness tester in the air | ASTM D573 | ||
| Shaw A, 135 ℃, 1000 hr | 1.0 | ASTM D573 | |
| Shaw A, 150 ℃, 168 hr | -1.0 | ASTM D573 | |
| The rate of change of Shore hardness in air | ISO 188 | ||
| Shaw A, 135 ℃, 1000 hr | 1.0 | ISO 188 | |
| Shaw A, 150 ℃, 168 hr | -1.0 | ISO 188 | |
| Volume change | |||
| 125 ℃, 70 hr, in IRM 903 oil | 73 | % | ISO 1817 |
| 125 ℃, 70 hr, in IRM 903 oil | 73 | % | ASTM D471 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.5 mm，Black Color | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Apparent viscosity of melt – Capillary @ 206/s | |||
| 200℃ | 330 | Pa·s | ISO 11443 |
| 200℃ | 330 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Barrel rear temperature | 177 to 216 | °C | |
| Barrel middle temperature | 177 to 216 | °C | |
| Barrel front temperature | 177 to 216 | °C | |
| Nozzle temperature | 188 to 221 | °C | |
| Processing (melt) temperature | 182 to 221 | °C | |
| Mold temperature | 10 to 66 | °C | |
| Back pressure | 0.0689 to 1.03 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Screw length to diameter ratio | 20.0:1.0 | ||
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Barrel 1 zone temperature | 182 to 204 | °C | |
| Barrel 2 zone temperature | 182 to 204 | °C | |
| Barrel 3 zone temperature | 188 to 210 | °C | |
| Barrel 4 zone temperature | 188 to 210 | °C | |
| Melt temperature | 193 to 216 | °C | |
| Nozzle temperature | 193 to 216 | °C | |
| Traction roller | 21 to 49 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method Ba, Angle (Unnicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |