| About |
|---|
| Description Halogen Free Flame Retardant, High Heat Resistance Application IT/OA Housing and Components (Adaptor)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | V-0,High Heat Resistance,Flame Characteristics,Halogen free |
| Availabilitys | Europe,Latin America,Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ASTM D1238 |
| Molding shrinkage | |||
| MD：3.2 mm | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23℃，3.2mm | 760 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed, 6.4 mm | 130 | ℃ | ASTM D648 |
| Vicat Softening Temperature | 140 | ℃ | ASTM D1525 5 |
| Relative Temperature Index (RTI) | |||
| Electrical performance | 120 | ℃ | UL 746 |
| Strength mechanical performance | 120 | ℃ | UL 746 |
| Impact mechanical performance | 115 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | UL 94 | ||
| 1.00 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 5VA | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld, 3.20 mm | 61.8 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK, 3.20 mm | > 100 | % | ASTM D638 |
| Flexural Modulus | |||
| 3.20 mm | 2260 | MPa | ASTM D790 |
| Flexural Strength | |||
| Yield yld, 3.20 mm | 95.1 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Maximum Moisture Content | < 0.020 | % | |
| Rear Temperature Zone 1 | 260 to 280 | °C | |
| Middle Temperature Zone 2 | 280 to 300 | °C | |
| Front Temperature Zone 3 | 300 to 320 | °C | |
| Nozzle temperature | 300 to 320 | °C | |
| Melt Temperature | 300 to 320 | °C | |
| Mold Temperature | 80 to 120 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.39 in/min |
| 4. 18.6kg |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |