| About |
|---|
| NORYL GTX934 is an unfilled GTX grade with improved processability and heat ageing performance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Negative |
| Features | Excellent Processability,Good heat aging resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 13 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD | 1.6 to 2.0 | % | Internal Method |
| MD：3.2 mm | 1.4 to 1.7 | % | Internal Method |
| TD：3.2 mm | 1.1 to 1.4 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 3.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.2 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 100 | J/m | ASTM D256 |
| 23℃ | 220 | J/m | ASTM D256 |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 20 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 60.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 190 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 190 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| B120 | 205 | ℃ | ASTM D1525 11 , ISO 306/B120 11 |
| A50 | 250 | ℃ | ISO 306/A50 |
| B50 | 200 | ℃ | ISO 306 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.5E-5 | 1/℃ | ASTM E831 |
| MD：23~60℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 8.5E-5 | 1/℃ | ASTM E831 |
| TD：23~60℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.23 | W/m/K | ISO 8302 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 85.0 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 2300 | MPa | ASTM D638 |
| — | 2400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 65.0 | MPa | ASTM D638 |
| yield | 65.0 | MPa | ISO 527-2/50 |
| fracture | 55.0 | MPa | ASTM D638 |
| fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ASTM D638 |
| yield | 4.5 | % | ISO 527-2/50 |
| fracture | 60 | % | ASTM D638 |
| fracture | 25 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2350 | MPa | ASTM D790 |
| — | 2200 | MPa | ISO 178 |
| bending strength | |||
| — | 90.0 | MPa | ISO 178 |
| Yield, 50 mm span | 95.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 290 to 320 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 290 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |