| About |
|---|
| LEXAN™ CFR5630 resin LEXAN™ CFR5630 Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density and 60 second vertical burn and OEM toxicity requirements. LEXAN CFR5630 resin is available in transparent and opaque colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low smoke,Halogen free,Flame Characteristics,Low toxicity |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.19 | g/cm³ | ASTM D792 |
| — | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 5.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 5.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.55 to 0.75 | % | |
| TD：3.2 mm | 0.60 to 0.80 | % | |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.14 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.11 | % | |
| Weathering resistance | f1 | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2500 | MPa | ASTM D638 |
| — | 2400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 68.0 | MPa | ASTM D638 |
| yield | 67.0 | MPa | ISO 527-2/50 |
| fracture | 52.0 | MPa | ASTM D638 |
| fracture | 52.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | 51 | % | ASTM D638 |
| fracture | 23 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2400 | MPa | ASTM D790 |
| — | 2500 | MPa | ISO 178 |
| bending strength | |||
| — | 103 | MPa | ISO 178 |
| Yield, 50 mm span | 106 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 9.0 | kJ/m² | |
| 23℃ | 10 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 130 | kJ/m² | |
| 23℃ | 130 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 85 | J/m | ASTM D256 |
| 23℃ | 100 | J/m | ASTM D256 |
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -30℃ | 2000 | J/m | ASTM D4812 |
| 23℃ | 2200 | J/m | ASTM D4812 |
| -30℃ | 无断裂 | ISO 180/1U | |
| 23℃ | 无断裂 | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 66.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 131 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 131 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 120 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 120 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| — | 136 | ℃ | ASTM D1525 18 |
| B50 | 137 | ℃ | ISO 306 |
| B120 | 139 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 6.6E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.2E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 7.6E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 125 | ℃ | UL 746 |
| Electrical performance | 125 | ℃ | UL 746 |
| Impact mechanical performance | 120 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1.10 GHz | 2.79 | ASTM ES7-83 | |
| Dissipation factor | |||
| 1.1 GHz | 5.8E-3 | ASTM ES7-83 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 875 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 45 | % | ISO 4589-2 |
| FAA Flammability | PASSES | FAR 25.853 | |
| NBS smoke density | |||
| Flaming，Dmax | 70.0 | ASTM E662 | |
| Vertical combustion test | FAR 25.853 | ||
| Test a 60 s，passes at | 5.0 | sec | |
| Test b 12 s，passes at | 5.0 | sec |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 266 to 288 | °C | |
| Barrel middle temperature | 277 to 299 | °C | |
| Barrel front temperature | 288 to 310 | °C | |
| Nozzle temperature | 282 to 304 | °C | |
| Processing (melt) temperature | 288 to 310 | °C | |
| Mold temperature | 71.1 to 93.3 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |