NORYL™ FE1740PW resin

About
Noryl* FE1740PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; this grade has been developed for fluid engineering applications where higher static stiffness is required. Noryl* FE1740PW has been certified for potable water applications up to 85C in Europe and North America in limited colours.&&

About

Noryl* FE1740PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; this grade has been developed for fluid engineering applications where higher static stiffness is required. Noryl* FE1740PW has been certified for potable water applications up to 85C in Europe and North America in limited colours.&&

Product Description
Supplier	SABIC
Generic	PPO(PPE)+PS
Material Status	Commercial: Active
Features	Good Rigidity,Hydrolysis stability
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.40	g/cm³	ASTM D792
Density	1.40	g/cm³	ISO 1183
Melt Flow Rate
300℃，5.0kg	10	g/10min	ASTM D1238
Melt Volume Rate
300℃，10 kg	20.0	cm³/10min	ISO 1133
Shrinkage rate
MD：3.2 mm	0.090 to 0.15	%	Internal Method
Water absorption rate
Saturation, 23 ℃	0.20	%	ISO 62
Equilibrium, 23 ℃, 50% RH	0.060	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	13800	MPa	ASTM D638
Tensile modulus	11300	MPa	ISO 527-1-2
tensile strength
fracture	155	MPa	ISO 527-2/5
fracture	165	MPa	ASTM D638
Tensile strain
fracture	1.8	%	ISO 527-2/5
fracture	1.8	%	ASTM D638
Bending modulus	9500	MPa	ISO 178
50 mm span	11700	MPa	ASTM D790
bending strength	195	MPa	ISO 178
bending strength
Fracture, 50 mm span	225	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
23℃	30	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch			ASTM D256
-30℃	90	J/m	ASTM D256
23℃	110	J/m	ASTM D256
Notched impact strength of cantilever beam			ISO 180/1U
-30℃	30	kJ/m²	ISO 180/1U
23℃	30	kJ/m²	ISO 180/1U
Dart impact equipped with measuring instruments
23℃，Total Energy	18.0	J	ASTM D3763

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed, 64 mm span	147	℃	ISO 75-2/Af
1.8 MPa, unannealed, 3.2 mm	148	℃	ASTM D648
Vicat Softening Temp	151	℃	ASTM D1525 10
Vicat Softening Temp
B50	152	℃	ISO 306
B120	161	℃	ISO 306/B120
Linear coefficient of thermal expansion
TD：-40~40℃	7.0E-5	1/℃	ISO 11359-2
MD：-40~40℃	2.0E-5	1/℃	ISO 11359-2

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	100 to 120	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.020	%
Hopper temperature	60 to 80	°C
Barrel rear temperature	250 to 270	°C
Barrel middle temperature	270 to 290	°C
Barrel front temperature	290 to 310	°C
Nozzle temperature	280 to 300	°C
Processing (melt) temperature	280 to 300	°C
Mold temperature	80 to 120	°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. 0.20 in/min
3. Type I, 0.20 in/min
4. 0.051 in/min
5. 0.079 in/min
6. at Break
7. 80104 sp=62mm
8. 80104 mm
9. Rate A (50°C/h), Loading 2 (50 N)
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.