| About |
|---|
| Polycarbonate crystal flame retardant (V-0) for injection molding with excellent thermal and mechanical properties, with UV protection.&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Flame Characteristics,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 12 to 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| balance | 0.16 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 90 | % | ASTM D638 |
| Bending modulus | 2200 | MPa | ASTM D790 |
| bending strength | 89.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 135 | ℃ | ASTM D648 |
| Vicat Softening Temp | 155 | ℃ | ASTM D1525 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric strength | 19 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 265 to 290 | °C | |
| Mold temperature | 70 to 110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |