| Description Heat Resistance Applications Automotives Interior Housing (Switch Panel Housing etc)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 4.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 78 | J/m | |
| -30℃，6.4mm | 69 | J/m | |
| 23℃，3.2mm | 180 | J/m | |
| 23℃，6.4mm | 170 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 115 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 106 | ℃ | |
| Vicat Softening Temp | 116 | ℃ | ASTM D1525 5 |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.5E+3 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1 mm | 33 | kV/mm | ASTM D149 |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 111 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.20 mm | 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 20 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2450 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 77.5 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 90.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.070 | % | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 200 to 220 | °C | |
| Barrel front temperature | 220 to 230 | °C | |
| Nozzle temperature | 220 to 230 | °C | |
| Processing (melt) temperature | 190 to 210 | °C | |
| Mold temperature | 40.0 to 60.0 | °C | |
| Back pressure | 0.981 to 2.94 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |