Clariant Nylon 6/6 66G33-L

About
Clariant Nylon 6/6 66G33-L is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in North America for injection molding. Important attributes of Clariant Nylon 6/6 66G33-L are: Flame Rated Lubricated&&

Product Description
Supplier	Clariant
Generic	PA66
Material Status	Commercial: Active
Features	Lubricating,HB
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.37	g/cm³	ASTM D792
Shrinkage rate
MD	0.30 to 0.70	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
tensile strength	145	MPa	ASTM D638
Tensile strain
fracture	4.0	%	ASTM D638
Bending modulus	8270	MPa	ASTM D790
bending strength	193	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	64	J/m	ASTM D256
Tensile impact strength	58.8	kJ/m²	ASTM D1822

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	253	℃	ASTM D648
1.8 MPa, unannealed	248	℃	ASTM D648
Melting temperature	257	℃
1.6 mm	105	℃	UL 746
3.2 mm	110	℃	UL 746
6.1 mm	110	℃	UL 746
1.6 mm	65.0	℃	UL 746
3.2 mm	65.0	℃	UL 746
6.1 mm	65.0	℃	UL 746
Relative temperature index			UL 746
Electrical performance			UL 746
Impact mechanical performance			UL 746
1.60 mm	105	℃	UL 746
3.20 mm	110	℃	UL 746
6.10 mm	110	℃	UL 746

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level		UL 94
1.60 mm	HB	UL 94
3.20 mm	HB	UL 94
6.10 mm	HB	UL 94

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	71 to 82	°C
Proposed maximum recycled material ratio	25	%
Barrel rear temperature	249 to 271	°C
Barrel middle temperature	271 to 288	°C
Barrel front temperature	282 to 299	°C
Nozzle temperature	266 to 288	°C
Mold temperature	71 to 104	°C
Injection pressure	55.2 to 138	MPa
Back pressure	0.00 to 1.03	MPa
Screw speed	30 to 60	rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.