| CHARACTERISTIC PROPERTIES High hardness. Good flow characteristics. Low deformation. MAJOR APPLICATIONS Containers. Components for machine building. Lids.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good liquidity,Good Hardness,High density |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 to 0.964 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 6.0 to 10 | g/10min | ISO 1133 |
| 190℃，5.0kg | 20 to 26 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 80 ℃, 2% surfactant | 1.50 | hr | ISO 16770 |
| Volatiles | < 0.30 | wt% | |
| Melt flow ratio | 2.50 to 3.70 | ||
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | > 2.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -80.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | |||
| B50 | 72.0 | ℃ | ISO 306 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ISO 868 | |
| Tensile modulus | |||
| Secant, 23 ℃ | 1350 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 29.0 | MPa | ISO 527-2/50 |
| fracture | 30.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2 |
| fracture | > 1000 | % | ISO 527-2/50 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 280 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. @ 2.5 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |