| Flexible, non-halogenated FR mPPE extrusion grade ideal for evaluation in applications such as wire insulation. Flame retardant performance capable of meeting VW1 and 105C temperature rating requirements as defined by UL 1581. 56 Shore D hardness. Excellent processing using standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+TPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Halogen free,Flame Characteristics |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，10.0kg | 5.1 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 23℃，48hr | 0.10 | % | ASTM D570 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 25 | kN/m | ISO 6383 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 85.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -40.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | |||
| A50 | 102 | ℃ | ISO 306/A50 |
| UL temperature rating | 105 | ℃ | UL 1581 |
| Heat Deformation（121℃） | 26 | % | UL 1581 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 3.9E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm in oil | 26 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 50 Hz | 2.60 | ||
| 60 Hz | 2.60 | ||
| 1 MHz | 2.50 | ||
| Dissipation factor | |||
| 50 Hz | 0.024 | ||
| 60 Hz | 0.024 | ||
| 1 MHz | 3.8E-3 | ||
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 750 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| VW-1 | Pass | UL 1581 | |
| Smoke density | |||
| Flaming，Ds max：500.0 µm | 150 | ||
| Non-Flaming，Ds max：500.0 µm | 75 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 56 | ISO 868 | |
| tensile strength | |||
| fracture | 33.0 | MPa | UL 1581 |
| fracture | 23.0 | MPa | ASTM D638 |
| Fracture, 136 ℃ | 36.0 | MPa | UL 1581 |
| fracture | 23.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 200 | % | UL 1581 |
| fracture | 85 | % | ASTM D638 |
| Fracture, 136 ℃ | 160 | % | UL 1581 |
| fracture | 90 | % | ISO 527-2/50 |
| Bending modulus | |||
| 100 mm span | 650 | MPa | ASTM D790 |
| — | 720 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 3. Type I, 2.0 in/min |
| 4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 6. 0.49 in/min |
| 7. 2.0mm wire with 0.12 mm x 20 stranded copper |
| 8. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
| 9. Plaque |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |