| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Electrostatic discharge protection,Flame Characteristics,EMI,RFI,Antistatic property,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.20 to 0.30 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2070 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 86.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 5.0 to 10 | % | ASTM D638 |
| Bending modulus | 2760 | MPa | ASTM D790 |
| bending strength | 172 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 6.4mm, injection molding | 91 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35 mm | 139 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.35 mm | 133 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 5.0E+8 to 5.0E+12 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | Internal Method | ||
| 0.79 mm | V-0 | Internal Method | |
| 1.50 mm | V-0 | Internal Method | |
| 3.20 mm, black | V-0 | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 130 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 290 to 310 | °C | |
| Barrel middle temperature | 290 to 310 | °C | |
| Barrel front temperature | 290 to 310 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |