CYCOLOY™ CM6220 Resin

About
CYCOLOY™ CM6220 树脂是一种矿物填充，高模量 (6GPa),高流动性和延展性，低翘曲聚碳酸酯树脂，非氯化，非溴化阻燃级别，满足薄壁阻燃性和不同的环境要求。

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Features	Low warping,High liquidity,Ductility,High modulus
Availabilitys	Asia Pacific

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, Type I, 50 mm/min	55	MPa	ASTM D638
tensile strength
Fracture, Type I, 50 mm/min	34	MPa	ASTM D638
Tensile strain
Yield, Type I, 50 mm/min	3	%	ASTM D638
Tensile strain
Fracture, Type I, 50 mm/min	15	%	ASTM D638
Tensile modulus
50 mm/min	5850	MPa	ASTM D638
bending strength
Yield, 50 mm span	98	MPa	ASTM D790
Bending modulus
2 mm/mim	6150	MPa	ISO 178
1.3 mm/min，50mm跨距	6030	MPa	ASTM D790
Rockwell hardness
R-level	109
tensile strength
Fracture, 50 mm/min	30	MPa	ISO 527
Yield, 50 mm/min	56	MPa	ISO 527
Tensile strain
Fracture, 50 mm/min	6	%	ISO 527
Yield, 50 mm/min	3	%	ISO 527
Tensile modulus
1 mm/min	5570	MPa	ISO 527
bending strength
Yield, 2 mm/min	98	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	95	J/m	ASTM D256
Impact strength of cantilever beam notch
-30℃	52	J/m	ASTM D256
Total energy of instrument impact
23℃	30	J	ASTM D 3763
Charpy Notched Impact Strength
23 ℃, 80 * 10 * 4, 62mm span	7	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	98	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, unannealed, 64 mm span	87	℃	ISO 75/Af
1.8 MPa, unannealed, 3.2 mm	85	℃	ASTM D648
0.45 MPa, unannealed, 3.2 mm	92	℃	ASTM D648
Linear coefficient of thermal expansion
TD：23~80℃	7.2E-05	1/℃	ISO 11359-2
MD：23~80℃	3.4E-05	1/℃	ISO 11359-2

PHYSICAL	Nominal value	Unit
Density	1.39
Shrinkage rate
MD：3.2 mm	0.2 – 0.3	%
Melt Flow Rate
300℃，1.20kg	12	g/10min
Density	1.4	g/cm³

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94V-1 flame level	0.8	mm	UL 94
94V-0 flame level	1.5	mm	UL 94
Flame retardant rating, 94V-5VB flame rating	1.5	mm	UL 94

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	85 – 95	°C
Drying time	4 – 6	hrs
Drying time (cumulative)	16	hrs
Melt temperature	255 – 285	°C
Nozzle temperature	255 – 285	°C
Front Section Zone 3 Temperature	255 – 285	°C
Temperature in Zone 2 of the middle section	255 – 285	°C
Temperature in Zone 1 of the rear section	245 – 280	°C
Mold temperature	70 – 90	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.