| Kingfa PA6-T25是一种聚酰胺6（尼龙6）材料,含有的填充物为25% 矿物填料。 该产品在亚太地区或北美洲有供货,加工方式为:注射成型。 Kingfa PA6-T25的主要特性有: 阻燃/额定火焰 抗翘曲 典型应用领域包括: 体育用品 工具 汽车行业 电气用具&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High elastic |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.90 | % | ASTM D995 |
| TD | 1.30 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，24hr | 0.60 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 212 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 165 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+16 | Ω.cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 65 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 117 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 80 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 10 | % | ASTM D638 |
| bending strength | |||
| 23℃ | 120 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 4700 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |