| About |
|---|
| Matrixx TPP1B30 is a Polypropylene product filled with 30% talc. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.70 to 1.1 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 31.7 | MPa | ASTM D638 |
| Bending modulus | |||
| tangent | 3030 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 27 | J/m | ASTM D256 |
| Drop hammer impact | < 1.13 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 73.9 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 127 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Strength mechanical performance | 65.6 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 104 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 177 to 221 | °C | |
| Barrel middle temperature | 177 to 221 | °C | |
| Barrel front temperature | 177 to 221 | °C | |
| Processing (melt) temperature | 199 to 227 | °C | |
| Mold temperature | 21 to 49 | °C | |
| Injection speed | Moderate | ||
| Back pressure | 0.138 to 2.07 | MPa | |
| Cushion | 6.35 to 12.7 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |