| About |
|---|
| (DOMAMID 6G30GT96M) Polyamide 6, 30% glass fiber reinforced, flame retardant, halogen and red phosphorous free, for injection moulding&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Low to no phosphorus content |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | |
| Shrinkage rate | |||
| TD：23℃，72 hrs | 0.60 to 0.80 | % | |
| MD：23℃，72 hrs | 0.40 to 0.60 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6600 | MPa | |
| tensile strength | |||
| fracture | 90.0 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % | |
| Bending modulus | 6100 | MPa | |
| bending strength | 145 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.5 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.5 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| 23℃ | 35 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | |
| 1.8 MPa, unannealed | 175 | ℃ | |
| Vicat Softening Temp | 210 | ℃ | |
| Melting temperature | 221 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm | |
| Compared to the leakage tracing index | |||
| Solution A | 550 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | < 100 | mm/min | |
| Flame retardant level | |||
| 0.80 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glowing wire flammability index | |||
| 1.0-3.0 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | |||
| 1-3 mm | 700 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50% RH |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |