| PP with flame retardant, antimony-, chlorine- and bromine free according IEC 61249-2-21, heat stabilsed&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,No antimony,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 to 1.11 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | > 18.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 |
| Bending modulus | > 2200 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | > 1.5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | > 55 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 112 | ℃ | ISO 75-2/B |
| Relative temperature index | |||
| Electrical performance | 120 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| 0.4 mm | 2.9E+13 | ohms | |
| 1 mm | 5.4E+13 | ohms | |
| Volume resistivity | |||
| 0.40 mm | > 4.5E+15 | ohms·cm | |
| 1.0 mm | > 1.8E+15 | ohms·cm | |
| Dielectric strength | |||
| 0.125 mm | 56 | kV/mm | IEC 60243-1 |
| 0.4 mm | 70 | kV/mm | IEC 60243-2 |
| Compared to the leakage tracing index | PLC 0 | ASTM D3638 | |
| High Arc Burning Index (HAI) (0.40 to 1.10 mm) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | |||
| 0.40 to 0.90 mm | PLC 2 | ||
| 1.0 to 1.1 mm | PLC 0 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.40-1.10 mm | V-0 | ||
| 0.13-0.25 mm | VTM-0 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |