| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Heat Resistance, Good |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | ASTM D792 | |
| Shrinkage rate | |||
| MD | 0.5~0.8 | % | |
| Melt Flow Rate | |||
| 220℃，10.0kg | 4.5 | g/10min | ASTM D792 |
| Viscosity (260 ° C, 1000 sec-1) | 2250 | poise | ASTM D 3825 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 45 | MPa | ASTM D638 |
| Tensile modulus | 2200 | MPa | ASTM D638 |
| bending strength | |||
| yield | 77 | MPa | ASTM D790 |
| Bending modulus | 2410 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 109 | ASTM D785 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa，3.2 mm | 106 | ||
| 1.8 MPa，3.2 mm | 92 | ℃ | ASTM D648 |
| 1.8 MPa，6.4 mm | 98 | ℃ | ASTM D648 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 240 | J/m | ASTM D256 |
| Instrument impact energy peak (23 ° C) | 13 | J | ASTM D 3763 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Dry conditions | Nominal value | Unit | Test method |
| Melt Temperature | 240~260 | ℃ | |
| Mold temperature | 60~80 | ℃ | |
| drying temperature | 90~100 | ℃ | |
| Drying time | 2~4 | hrs | |
| Drying time (cumulative) | 8 | hrs | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |