| 20% glass fibres reinforced injection moulding grade with superior mechanical properties&& |
| Product Description | |
|---|---|
| Generic | PBT+ASA |
| Material Status | Commercial: Negative |
| Features | HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 6900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 100 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.8 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 49 | kJ/m² | ISO 179/1eU |
| 23℃ | 60 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 200 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 160 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 223 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 4.0E-5 | 1/℃ | DIN 53752 |
| Maximum operating temperature | |||
| 20000 h | 140 | ℃ | IEC 216 |
| some hours | 160 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 25 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 3.60 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.019 | IEC 60250 | |
| Compared to the leakage tracing index | 450 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 130 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 250 to 275 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test Specimen accordng to ISO 3167, Type A |
| 3. 80x10x4 mm |
| 4. 110x10x4 mm |
| 5. 10 K/min, Compound for moulding |
| 6. >10x10x4 mm |
| 7. 80x80x1 mm |
| 8. 125x13x0.8 mm |
| 9. 125x13x1.6 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |