Adiprene® L 700

About
ADIPRENE L 700 is a TDI polyether-based liquid urethane prepolymer which is readily processable by conventional hand and machine mixing techniques. ADIPRENE L 700 produces high quality elastomers in the 90-94 A durometer (42-46 D durometer) hardness range when cured with 4,4′-methylene-bis (2-chloroaniline) or Chemtura’s CAYTUR® 21 urethane curative. These tough, highly resilient elastomers have many unique features: Excellent low-temperature flexibility Excellent abrasion resistance Good hydrolytic stability Good compression set resistance These properties suggest the use of ADIPRENE L 700 in applications such as wheels, rolls, or spraying.&&

About

ADIPRENE L 700 is a TDI polyether-based liquid urethane prepolymer which is readily processable by conventional hand and machine mixing techniques. ADIPRENE L 700 produces high quality elastomers in the 90-94 A durometer (42-46 D durometer) hardness range when cured with 4,4′-methylene-bis (2-chloroaniline) or Chemtura’s CAYTUR® 21 urethane curative. These tough, highly resilient elastomers have many unique features: Excellent low-temperature flexibility Excellent abrasion resistance Good hydrolytic stability Good compression set resistance These properties suggest the use of ADIPRENE L 700 in applications such as wheels, rolls, or spraying.&&

Product Description
Supplier	Chemtura
Generic	PUR-脂肪族+TDI
Material Status	Commercial: Active
Features	Good flexibility,Hydrolysis stability,Elastic,Low temperature toughness,Good wear resistance
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.12	g/cm³	ASTM D792

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	92		ASTM D2240

elastic body	Nominal value	Unit	Test method
tensile strength			ASTM D412
100% strain	9.65	MPa	ASTM D412
300% strain	21.4	MPa	ASTM D412
tensile strength	37.2	MPa	ASTM D412
tear strength
cracking	19	kN/m	ASTM D470
Compression deformation
70℃，22 hr	31	%	ASTM D395B
Basho’s elasticity	40	%	ASTM D2632
Kappa’s modulus			ASTM D1043
-57℃	296	MPa	ASTM D1043
-40℃	117	MPa	ASTM D1043
-18℃	40.7	MPa	ASTM D1043
24℃	26.2	MPa	ASTM D1043

THERMAL	Nominal value	Unit
Thermosetting components
resin	按重量计算的混合比: 100
Hardening method	按重量计算的混合比: 17
storage stability	3.0	min
Post curing time
70℃	16	hr

Supplementary information	Nominal value	Unit	Test method
friction coefficient
NBS	230

Uncured Properties	Nominal value	Unit	Test method
Curing time
100℃	1.0	hr

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.