| About |
|---|
| CALIBRE™ 603-2 Resin is specially designed for extrusion of super heavy wall sheet and very complex profiles. This resin offers exceptional high melt strength for effective calibration of complex structures, and excellent surface quality. The resin is UV bulk stabilized, but for outdoor use, co-extrusion with a UV cap is needed. It is recommended to apply a 50 micron layer of CALIBRE™ 320UV. Applications Multi wall sheet extrusion and profile extrusion&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good melt strength,HB |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 1.8 | g/10min | ASTM D1238 |
| 300℃，1.20kg | 1.8 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 4 mm, injection molded | 2400 | MPa | ISO 527-2 |
| 4 mm, injection molded | 2350 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 4 mm, injection molded | 51.0 | MPa | ISO 527-2 |
| Fracture, 4 mm, injection molded | 51.0 | MPa | ASTM D638 |
| Yield, 4 mm, injection molding | 63.0 | MPa | ASTM D638 |
| Yield, 4 mm, injection molding | 63.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 4 mm, injection molded | 50 | % | ISO 527-2 |
| Fracture, 4 mm, injection molded | 50 | % | ASTM D638 |
| Yield, 4 mm, injection molding | 6.3 | % | ISO 527-2 |
| Yield, 4 mm, injection molding | 6.3 | % | ASTM D638 |
| Bending modulus | |||
| 4 mm, injection molded | 2400 | MPa | ISO 178 |
| 4 mm, injection molded | 2400 | MPa | ASTM D790 |
| bending strength | |||
| 4 mm, injection molded | 93.1 | MPa | ASTM D790 |
| bending strength | |||
| 4 mm, injection molded | 93.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23 ℃, injection molding | 69 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23 ℃, 4mm, injection molding | 800 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 127 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 127 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 140 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 140 | ℃ | ASTM D648 |
| Vicat Softening Temp | 146 | ℃ | ASTM D1525 2 |
| B50 | 146 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 2 (50 N) |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |