INNOPOL® CS 1-3820 GB is a 20 % glass-bead-filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 1-3820 GB is recommended for producing injection moulded products, where the required properties are good stiffness besides dimensional stability.&& |
Product Description | |
---|---|
Generic | PP homopolymerization |
Material Status | Commercial: Negative |
Features | Good Rigidity,Good Dimensional Stability,Homopolymer |
Availabilitys | Europe |
Process Methods | Injection Molding |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.04 | g/cm³ | ISO 1183 |
Melt Flow Rate | |||
230℃,2.16kg | 10 | g/10min | ISO 1133 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Tensile modulus | 1800 | MPa | ISO 527-2/2 |
tensile strength | |||
yield | 30.0 | MPa | ISO 527-2/50 |
Tensile strain | |||
yield | 5.0 | % | ISO 527-2/50 |
Bending modulus | 1900 | MPa | ISO 178 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Charpy Notched Impact Strength | |||
23℃ | 3.5 | kJ/m² | ISO 179/1eA |
Charpy Unnotch Impact strength | 30 | kJ/m² | ISO 179/1eU |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
0.45 MPa, unannealed | 120 | ℃ | ISO 75-2/B |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Drying temperature | 80 | °C | |
Drying time | 2.0 | hr | |
Recommended maximum moisture content | 0.070 | % | |
Barrel rear temperature | 190 to 240 | °C | |
Barrel middle temperature | 190 to 240 | °C | |
Barrel front temperature | 190 to 240 | °C | |
Processing (melt) temperature | 210 to 250 | °C | |
Mold temperature | 10 to 50 | °C |
Notes |
---|
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |