| About |
|---|
| HP-120NA is a Nucleated Polypropylene certified prime grade designed for injection molding general purpose applications. HP-120NA contains antistatic and combines a good balance of medium-high flow processability with good tensile strength, high stiffness and good contact clarity. HP-120NA recommended processing temperature is between 210° to 230°C with mold at 20°-50°C. HP-120NA complies with FDA regulation 21CFR 177.1520 and with most international regulations concerning the use of Polypropylene in contact with food.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,High liquidity,Nucleation,Food contact compliance,Good Tensile Strength,Antistatic property,Homopolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 35 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 116 | ℃ | ASTM D648 |
| Vicat Softening Temp | 155 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 95 | ASTM D785 | |
| tensile strength | |||
| yield | 37.2 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 9.0 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1770 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 210 to 230 | °C | |
| Mold temperature | 20 to 50 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |