| HWB-1051 is a certified prime grade Hexene copolymer High Molecular Weight developed for BLOW MOLDING of high performance medium to large size industrial containers. HWB-1051 features good processability, good melt strength, excellent combination of ESCR, high Impact strength, Stiffness, good Thermoform ability, and good chemical resistance. HWB-1051 applications include 20 to 55 gallon containers, chemical and gasoline tanks, carrying cases, automotive parts, tool boxes, truck-bed liners, and sheet, pipe and profile extrusion. HWB-1051 recommended processing temperature is 190 to 210°C.. HWB-1051 complies with FDA regulation 21CFR 177.1520 (c )3.1(a) + 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles.&& |
| Product Description | |
|---|---|
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Food contact compliance,Good melt strength,Copolymer,Solvent resistance,Hexene copolymers,High ESCR |
| Availabilitys | Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.060 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 10 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Molded into shape, F50 | > 1000 | hr | ASTM D1693 |
| 50 ℃, 1.75 mm, 10% non-ionic surfactant, molded, F50 | 150 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, molding | 24.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 800 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 1070 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | |||
| Compression Molding | 347 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 44.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -90.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 129 | ℃ | ASTM D1525 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blowing molding temperature | 190 to 210 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |