SLOVALEN® PH 81 C 40

About
Modified homopolymer and copolymer PP for injection moulding with the contenct of 40% microground, chemically modified talc. Increased strength, rigidity and thermal application up to 100°C depending on the talc content. Decreased shrinkage. Packing material, garden flower-pots, toys, dowels, clamps, hinge, office chairs, holders, covers of motors, chassis, protection trims in the automotive industry, electroinstallation boxes in the electrical industry. Fulfills the glow wire 750°C. Delivered in the full RAL colour scale.Higher ITT in comparison with PH 51 C 40.&&

About

Modified homopolymer and copolymer PP for injection moulding with the contenct of 40% microground, chemically modified talc. Increased strength, rigidity and thermal application up to 100°C depending on the talc content. Decreased shrinkage. Packing material, garden flower-pots, toys, dowels, clamps, hinge, office chairs, holders, covers of motors, chassis, protection trims in the automotive industry, electroinstallation boxes in the electrical industry. Fulfills the glow wire 750°C. Delivered in the full RAL colour scale.Higher ITT in comparison with PH 51 C 40.&&

Product Description
Generic	PP not specified
Material Status	Commercial: Active
Features	Good Rigidity,Copolymer,Homopolymer,HB
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.25	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	12	g/10min	ISO 1133
Shrinkage rate			STM 64 0808
TD	1.2	%	STM 64 0808
MD	1.2	%	STM 64 0808

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2300	MPa	ISO 527-2
tensile strength
yield	25.0	MPa	ISO 527-2
Tensile strain
yield	4.0	%	ISO 527-2
Bending modulus	2400	MPa	ISO 178
bending strength	40.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20℃	2.0	kJ/m²	ISO 179
23℃	4.0	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-20℃	15	kJ/m²	ISO 179
23℃	35	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	110	℃	ISO 75-2/B
Vicat Softening Temp	155	℃	ISO 306/B
Melting temperature
DSC	150	℃	ISO 3146

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94
Igniting temperature of the hot wire	750	℃	IEC 60695-2-13

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	200 to 250	°C
Mold temperature	40 to 60	°C
Injection pressure	70.0 to 120	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.