Braskem PE HC1828

About
HC1828 is a Linear Low Density Polyethylene, 1-hexene copolymer, produced by gas phase process. Developed for cast film extrusion. Films obtained with this product show high load retention, outstanding puncture and tear resistance, excellent optical properties and are recommended for automatic application. It contains antioxidant additive. Applications: Stretch films, liners, LLDPE and HDPE blends and packages for general use. Process: HC1828 must be processed in cast extruder, adjusted to this polymer. The excellent conditions of processing in accordance with the type of used equipment, but the best results are gotten with 220 to 270°C extrusion temperature.&&

About

HC1828 is a Linear Low Density Polyethylene, 1-hexene copolymer, produced by gas phase process. Developed for cast film extrusion. Films obtained with this product show high load retention, outstanding puncture and tear resistance, excellent optical properties and are recommended for automatic application. It contains antioxidant additive. Applications: Stretch films, liners, LLDPE and HDPE blends and packages for general use. Process: HC1828 must be processed in cast extruder, adjusted to this polymer. The excellent conditions of processing in accordance with the type of used equipment, but the best results are gotten with 220 to 270°C extrusion temperature.&&

Product Description
Supplier	Braskem
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Optical performance,Low density,Good tear strength
Availabilitys	Latin America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	2.8	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
tensile strength			ASTM D882
MD, fracture, 25 µ m	46.0	MPa
TD, fracture, 25 µ m	30.0	MPa
Tensile strain			ASTM D882
MD, fracture, 25 µ m	510	%
TD, fracture, 25 µ m	770	%
Bending modulus			ASTM D790
1% secant, MD, 25 µ m	147	MPa
1% secant, TD, 25 µ m	157	MPa
Drop hammer impact
25 µm	87	g	ASTM D1709
Elmandorf tear strength			ASTM D1922
MD：25 µm	44	g
TD：25 µm	150	g

optical performance	Nominal value	Unit	Test method
gloss
60°，25.0 µm	92		ASTM D2457
Haze	2.0	%	ASTM D1003

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.