| About |
|---|
| BM5225X resin is a mineral filled grade featuring of high modulus, good flow and ductility, low warpage. It is of non-Br & non-Cl flame retardant systems intended to meet thin wall flame resistance and various environmental requirements.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low warping,Ductility,Good liquidity,Halogen free,Flame Characteristics,V-1 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.39 | g/cm³ | ASTM D792 |
| — | 1.40 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.30 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 50 | J/m | |
| 23℃ | 90 | J/m | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 29.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 92.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 94.0 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 87.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | 98.0 | ℃ | ASTM D1525 13 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~80℃ | 3.4E-5 | 1/℃ | |
| TD：23~80℃ | 7.2E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-1 | ||
| 1.50 mm | V-0 5VB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 109 | ASTM D785 | |
| Tensile modulus | |||
| — | 5850 | MPa | ASTM D638 |
| — | 5570 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 55.0 | MPa | ASTM D638 |
| yield | 56.0 | MPa | ISO 527-2/5 |
| fracture | 34.0 | MPa | ASTM D638 |
| fracture | 30.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 3.0 | % | ASTM D638 |
| yield | 3.0 | % | ISO 527-2/5 |
| fracture | 15 | % | ASTM D638 |
| fracture | 6.0 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 6020 | MPa | ASTM D790 |
| — | 6160 | MPa | ISO 178 |
| bending strength | |||
| — | 98.0 | MPa | ISO 178 |
| Yield, 50 mm span | 98.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 to 105 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 16 | hr | |
| Barrel rear temperature | 250 to 270 | °C | |
| Barrel middle temperature | 260 to 280 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 70.0 to 90.0 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |