WELLAMID Nylon 6000/58 HWUVCP is a Polyamide 6 (Nylon 6) material. It is available in Europe. Important attributes of WELLAMID Nylon 6000/58 HWUVCP are: Flame Rated Heat Stabilizer Impact Modified UV Stabilized&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	High impact resistance,Weather resistance is good,Heat Stabilized
Availabilitys	Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile Stress
Yield yld, dry dry dry	50	MPa	ISO 527
Yield yld, wet cond	35	MPa	ISO 527
Tensile Strain
Yield yld, dry dry dry	5	%	ISO 527
Yield yld, wet cond	30	%	ISO 527
Broken BRK, dry dry	>50	%	ISO 527
Broken BRK, wet Cond	>50	%	ISO 527
Tensile Modulus
Dry	2200	MPa	ISO 527
Wet Cond	900	MPa	ISO 527
Flexural Modulus	1800	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23 ℃, dry	NB	kJ/m²	ISO 179
23 ℃, moist cond	NB	kJ/m²	ISO 179
-40 ℃, dry	NB	kJ/m²	ISO 179
Charpy Unnotch Impact strength
23 ℃, dry	25	kJ/m²	ISO 179
23 ℃, moist cond	65	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Melting temperature	223	℃
Hot deformation temperature HDT
A	45	℃	ISO 75-1/-2
B	100	℃	ISO 75-1/-2
Vicat Softening Temperature	170	℃	ISO 306/B
Coeff. of linear thermal expansion
23℃-80℃	0.9	×10-4/K	DIN 53752

ELECTRICAL	Nominal value	Unit	Test method
Relative permittivity
Dry	3.5	1 MHz	IEC 60250
Wet Cond	6	1 MHz	IEC 60250
Dissipation Factor
Dry	240	1 MHz	IEC 60250
Wet Cond	2500	1 MHz	IEC 60250
Electric strength
Dry	32	kV/mm	IEC 60243-1
Wet Cond	35	kV/mm	IEC 60243-1
Compared Tracking Index
Dry	600	V	IEC 60112
Volume Resistance
Dry	1E15	ohm·cm	IEC 60093
Wet Cond	1E12	ohm·cm	IEC 60093
Surface Resistivity
Dry	1E13	ohm	IEC 60093
Wet Cond	1E10	ohm	IEC 60093

PHYSICAL	Nominal value	Unit	Test method
Density	1.06	g/cm³	ISO 1183
Mold Shrinkage	0.8-1.2	%
Saturation value at	2.5-3.3	%	DIN 53495

FLAME CHARACTERISTICS	Nominal value	Test method
Flame Class Rating
1.6 mm	HB	UL 94
1.6 mm	HB	UL 94
3.2 mm	HB	UL 94
3.2 mm	HB	UL 94

Process Conditions
Injection Molding	Nominal value	Unit	Test method
Melt Temperature	245 to 260	°C
Mold Temperature	40 to 80	°C
Injection speed	快速

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.