| Aegis® H135ZP is a high viscosity nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to FDA requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermoforming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance.&& |
| Product Description | |
|---|---|
| Supplier | Honeywell |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High Viscosity,High Heat Resistance,Good wear resistance,Solvent resistance,Homopolymer |
| Availabilitys | North America |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 235℃，1.0kg | 1.2 | g/10min | ASTM D1238 |
| Water absorption rate | ASTM D570 | ||
| 24hr | 1.6 | % | ASTM D570 |
| saturated | 9.5 | % | ASTM D570 |
| balance | 2.7 | % | ASTM D570 |
| water content | < 0.080 | % | ASTM D6869 |
| Relative viscosity | |||
| @96% sulfuric acid | 3.75 | ||
| viscosity | |||
| FAV | 135 | ASTM D789 | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Elastic modulus | |||
| TD | 640 | MPa | ASTM D882 |
| MD | 660 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield | 30.0 | MPa | ASTM D882 |
| TD, yield | 30.0 | MPa | ASTM D882 |
| MD, fracture | 90.0 | MPa | ASTM D882 |
| TD, fracture | 90.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 330 | % | ASTM D882 |
| TD, fracture | 330 | % | ASTM D882 |
| Carbon dioxide transfer rate | |||
| 23℃ | 72.8 | cm³/m²/24 hr | ASTM D1434 |
| Nitrogen transfer rate | |||
| 23℃ | 14.0 | cm³/m²/24 hr | ASTM D1434 |
| Oxygen transfer rate | |||
| 23℃ | 40 | cm³/m²/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 38℃，100% RH | 990 | g/m²/24 hr | ASTM F1249 |
| tear strength | ASTM D1922 | ||
| MD，23℃ | 860 | N | ASTM D1922 |
| TD，23℃ | 990 | N | ASTM D1922 |
| Graves Tear | ASTM D1004 | ||
| MD：23℃ | 2170 | N | ASTM D1004 |
| TD：23℃ | 2380 | N | ASTM D1004 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 220 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture Index（23℃） | 470.000 | g/cm³ | |
| Puncture resistance | |||
| 23℃ | 1100 | g |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Barrel 1 zone temperature | 230 to 260 | °C | |
| Barrel 2 zone temperature | 230 to 260 | °C | |
| Barrel 3 zone temperature | 230 to 260 | °C | |
| Barrel 4 zone temperature | 230 to 260 | °C | |
| Barrel 5 zone temperature | 230 to 260 | °C | |
| Connector temperature | 260 to 266 | °C | |
| Melt temperature | 260 to 270 | °C | |
| Nozzle temperature | 260 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. ASTM D1306 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |