| About |
|---|
| SUPREME Specialty PS SP06425 9885是一种高抗冲聚苯乙烯产品,。 它可以通过注射成型进行加工,在北美洲、非洲和中东、欧洲或亚太地区有供货。 典型应用领域为:电气/电子应用。 特性包括: 阻燃/额定火焰 耐磨 高光泽度 耐冲击&& |
| Product Description | |
|---|---|
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Good liquidity,Low coefficient of friction,Good wear resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 50 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 90 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm, injection molded | 78.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 97.0 | ℃ | ASTM D1525 3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 3.20 mm | 105 | ASTM D785 | |
| tensile strength | |||
| 23 ℃, 3.20 mm, injection molding | 30.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.20 mm, injection molding | 40 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, 3.20 mm, injection molding | 2300 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, 3.20 mm, injection molding | 49.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 | hr | |
| Melt temperature | 250 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |