| Hostaform® XGC10XAP is a Polyacetalcopolymer reinforced with approx. 10% glass fibres. Compared to the Hostaform® C 9021 GV 1/10 Hostaform® XGC10XAP has a higher strength and lower emissions.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low odor |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 3.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 1.0 | % | |
| MD | 1.4 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4700 | MPa | ISO 527-2/1A |
| tensile strength | |||
| fracture | 110 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 4.9 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 4200 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 60 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 154 | ℃ | ISO 75-2/A |
| Melting temperature | 166 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 | 1/℃ | |
| TD | 8.0E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 170 to 180 | °C | |
| Barrel middle temperature | 180 to 190 | °C | |
| Barrel front temperature | 190 to 200 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Processing (melt) temperature | 190 to 210 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | 慢 | ||
| Back pressure | < 2.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |