| About |
|---|
| Solumer™ 8705L is an ethylene-octene copolymer produced via Nexlene™ technology. Solumer™ 8705L performs well in a wide range of general purpose thermoplastic elastomer applications and has excellent flow characteristics. Applications: General purpose thermoplastic elastomers Impact modification Wire and cable Footwear&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Material Status | Commercial: Active |
| Features | High liquidity,Block Copolymer,High impact resistance,Octene copolymer |
| Availabilitys | Asia Pacific,Europe,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.868 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.5 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 36 | MU | ASTM D1646 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Broken BRK | 105 | kg/cm² | ASTM D638 |
| Elongation at Break | 800 | % | ASTM D638 |
| Tensile Modulus | 32 | kg/cm² | ASTM D638 |
| Flexural Modulus | 155 | kg/cm² | ASTM D790 |
| Tear strength | 46 | kg/cm² | ASTM D624 |
| Shore hardness | |||
| 46 | Shore A | ASTM D2240 | |
| 74 | Shore D | ASTM D2240 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 62 | ℃ | SK |
| Glass Transition Temperature | -52 | ℃ | SK |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 3. Die C |
| 4. Compression Molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |