| About |
|---|
| LNP STAT-KON ULTEM_UC1200 is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Electrostatic discharge protection,High Heat Resistance,V-0 |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 7.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.30 to 0.50 | % | Internal Method |
| MD：3.2 mm | 0.12 to 0.22 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8140 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 131 | MPa | ASTM D638 |
| yield | 131 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 5.1 | % | ASTM D638 |
| yield | 5.1 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 50 mm span | 7830 | MPa | ASTM D790 |
| 100 mm span | 8270 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| Fracture, 50 mm span | 221 | MPa | ASTM D790 |
| Fracture, 100 mm span | 193 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 420 | J/m | ASTM D4812 |
| 23℃ | 37 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 6.21 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 213 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 209 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 210 | ℃ | ASTM D648 |
| Vicat Softening Temp | 214 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | |||
| TD | ASTM E831 | ||
| MD | ASTM E831 | ||
| -40 to 40 ℃ | 1.4E-5 | cm/cm/℃ | ASTM E831 |
| -20 to 150 ℃ | 1.4E-5 | cm/cm/℃ | ASTM E831 |
| -40 to 40 ℃ | 3.2E-5 | cm/cm/℃ | ASTM E831 |
| -20 to 150 ℃ | 4.0E-5 | cm/cm/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 105 | ℃ | UL 746 |
| Strength mechanical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0E+5 | ohms | ASTM D257 |
| Volume resistivity | 4.0E+2 | ohms·cm | ASTM D257 |
| High Arc Burning Index (HAI) | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 | |
| Electrostatic attenuation | 10 | msec | FTMS 101B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 360 to 404 | °C | |
| Barrel middle temperature | 371 to 421 | °C | |
| Barrel front temperature | 382 to 427 | °C | |
| Nozzle temperature | 377 to 421 | °C | |
| Processing (melt) temperature | 382 to 427 | °C | |
| Mold temperature | 135 to 163 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.10 in/min |
| 5. 0.051 in/min |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |