| Prisma 1410 is a high melt flow rate random copolymer, designed for injection moulding. This product exhibits exceptional transparency, very good stiffness/impact strength balance and excellent processability. Applications: High-transparency parts and packages. This product has excellent processability, high productivity, excellent balance stiffness / impact. Processing: Injection Moulding&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | PP copolymer |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Excellent Processability,Good Clarity,High impact resistance,High liquidity,Random copolymer |
| Availabilitys | Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 40 | g/10min | ASTM D1238，ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -20 ℃, injection molding | 15 | J/m | ASTM D256 |
| 23 ℃, injection molding | 50 | J/m | ASTM D256 |
| -20 ℃, injection molding | 1.3 | kJ/m² | ISO 180 |
| 23 ℃, injection molding | 2.8 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, injection molded | 81.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 82.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed, injection molded | 50.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 129 | ℃ | ISO 306/A , ASTM D1525 3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 1000 µ m, injection molding | 8.0 | % | ASTM D1003 |
| 1000 µ m, injection molding | 8.0 | % | ISO 13468-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 79 | ASTM D785 | |
| R-level | 80 | ISO 2039-2 | |
| tensile strength | |||
| Yield, injection molding | 29.0 | MPa | ASTM D638 |
| Yield, injection molding | 28.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, injection molding | 14 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| 1% cut, injection molding | 1000 | MPa | ASTM D790 |
| 1% cut, injection molding | 1050 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molded |
| 3. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |