| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | PP not specified |
| Material Status | Commercial: Negative |
| Features | High Heat Resistance,Good Dimensional Stability,Good surface appearance,Heat Stabilized,HB,High scratch resistance |
| Availabilitys | Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12.7 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：2.0 mm | 10 – 13 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，t=4mm | 42 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 133 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5, 3.0mmt | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 | |
| tensile strength | |||
| yield | 34 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 60 | % | ASTM D638 |
| Bending modulus | 2350 | MPa | ASTM D790 |
| bending strength | 55 | MPa | ASTM D790 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 71 | % | ASTM D523 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Temperature at the rear of the barrel | 170 – 190 | °C | |
| Temperature in the middle of the barrel | 180 – 200 | °C | |
| Front temperature of material barrel | 180 – 210 | °C | |
| Nozzle temperature | 180 – 210 | °C | |
| Mold temperature | 50 – 70 | °C | |
| Injection pressure | 39.2 – 68.6 | MPa | |
| Back pressure | 0.490 – 1.96 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |