| PP-EPDM-T15&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Sprayable,Good coloring,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.980 to 1.02 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 to 15 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| 23℃ | 9.0E-3 to 9.5E-3 | % | Internal Method |
| 80℃，30 min | 1.0E-3 to 1.5E-3 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 18.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 60 | % | ISO 527-2/50 |
| Bending modulus | 1300 | MPa | ISO 178 |
| bending strength | 24.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 40 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | ISO 75-2/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | ISO 3795 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Weathering resistance | 4.00 to 5.00 | SAE J1960 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 0.0 to 2.0 | hr | |
| Barrel rear temperature | 190 to 210 | °C | |
| Barrel middle temperature | 205 to 230 | °C | |
| Barrel front temperature | 215 to 240 | °C | |
| Processing (melt) temperature | 220 to 245 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |