| About |
|---|
| Greenflex FD 50 F is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced by Greenflex FD 50 F exhibit good optical and sealing properties, high flexibility and toughness. Main Application Greenflex FD 50 F is recommended for the production of agricultural films and water proofing membrane having outstanding mechanical performances (flexibility, elasticity and adherence) and dimensional stability.&& |
| Product Description | |
|---|---|
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good heat sealing,Good Dimensional Stability,High elastic,Optical performance,Food contact compliance,Good bond,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.40 | g/10min | ISO 1133 |
| Vinyl acetate content | 17.0 | wt% | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw A, injection molding | 90 | ISO 868 | |
| Shaw’s D, injection molding | 39 | ISO 868 | |
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | 30 to 150 µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, blow molded film | 55.0 | MPa | ISO 527-3 |
| 1% secant, TD, blow molded film | 60.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, blow molded film | 4.50 | MPa | ISO 527-3 |
| TD, yield, blow molded film | 4.00 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, blow molded film | 35.0 | MPa | ISO 527-3 |
| TD, fracture, blow molded film | 30.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, blow molded film | 450 | % | ISO 527-3 |
| TD, fracture, blow molded film | 700 | % | ISO 527-3 |
| Drop hammer impact | |||
| Blown film | > 700 | g | ISO 7765-1/A |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD | 20.0 | kN/m | ISO 6383-2 |
| TD | 44.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -80.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 67.0 | ℃ | ISO 306/A |
| Melting temperature | 88.0 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, blow molded film | 87 | ASTM D2457 | |
| Haze | |||
| Blown film | 1.0 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |