| Polyamide 66 (PA66) based compound. Heat stabilised. Glass fibres. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free.&& |
| Product Description | |
|---|---|
| Supplier | LATI |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Heat Stabilized,Flame Characteristics,V-0,Halogenated |
| Availabilitys | Latin America,North America,Asia Pacific,Europe,Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：2.0 mm | 0.70-1.0 | % | ISO 294-4 |
| MD：2.0 mm | 0.35-0.60 | % | ISO 294-4 |
| Water Absorption | |||
| 23℃，24hr | 0.25 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23℃ | 9200 | MPa | ISO 527-1-2 |
| 60℃ | 7200 | MPa | ISO 527-1-2 |
| 90℃ | 4800 | MPa | ISO 527-1-2 |
| 120℃ | 3200 | MPa | ISO 527-1-2 |
| 150℃ | 2200 | MPa | ISO 527-1-2 |
| Tensile Strength | ISO 527-2/5 | ||
| Yield, 120 ℃ | 60.0 | MPa | ISO 527-2/5 |
| Yield, 150 ℃ | 50.0 | MPa | ISO 527-2/5 |
| Fracture, 23 ℃ | 135 | MPa | ISO 527-2/5 |
| Fracture, 60 ℃ | 95.0 | MPa | ISO 527-2/5 |
| Fracture, 90 ℃ | 75.0 | MPa | ISO 527-2/5 |
| Fracture, 120 ℃ | 60.0 | MPa | ISO 527-2/5 |
| Fracture, 150 ℃ | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 120 ℃ | 3.5 | % | ISO 527-2/5 |
| Yield, 150 ℃ | 3.7 | % | ISO 527-2/5 |
| Fracture, 23 ℃ | 2.1 | % | ISO 527-2/5 |
| Fracture, 60 ℃ | 2.4 | % | ISO 527-2/5 |
| Fracture, 90 ℃ | 3.8 | % | ISO 527-2/5 |
| Fracture, 120 ℃ | 3.9 | % | ISO 527-2/5 |
| Fracture, 150 ℃ | 4.2 | % | ISO 527-2/5 |
| Tensile Elongation | |||
| 120℃ | 3.5 | % | ISO 527 |
| 150℃ | 3.7 | % | ISO 527 |
| 23℃ | 2.1 | % | ISO 527 |
| 60℃ | 2.4 | % | ISO 527 |
| 90℃ | 3.8 | % | ISO 527 |
| 120℃ | 3.9 | % | ISO 527 |
| 150℃ | 4.2 | % | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed | 255 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 240 | ℃ | ISO 75-2/A |
| Continuous use temperature | 115 | ℃ | |
| Vicat Softening Temperature | |||
| B50 | 245 | ℃ | ISO 306 |
| Coeff. of linear thermal expansion | |||
| MD：30~100℃ | 8.0E-6 | 1/℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared Tracking Index | |||
| Solution A | 400 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index GWFI | IEC 60695-2-12 | ||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (GWIT) | IEC 60695-2-13 | ||
| 1 mm | 900 | ℃ | IEC 60695-2-13 |
| 2 mm | 900 | ℃ | IEC 60695-2-13 |
| Oxygen Index | 35 | % | ASTM D2863 |
| Supplementary Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Dimensional stability | 21.0 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60 MPa |
| 3. 20000 hr |
| 4. Without surfactant |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |