| About |
|---|
| Benefits & Features ELTEX® P KF359 is a random terpolymer with a high content of co-monomer especially designed for the blown film process, it contains no technical additive. It is thus particularly appreciated by users wishing to use their own “formulas”. Low sealing initiation temperature Broad sealing window Good stiffness level Barefoot version&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Terpolymer,Low temperature heat sealing |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.895 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.2 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃ | 57 | ISO 868 | |
| tensile strength | |||
| Yield, 23 ℃ | 20.0 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 500 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat Seal Threshold | 105 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 50.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 107 | ℃ | ISO 306/A50 |
| Melting peak temperature | 131 | ℃ | ASTM D3417 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1s, 3 bars, 100 mm/min, 100 g/cm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |