| About |
|---|
| A patented alloy of DuPont™ Surlyn® resin and nylon 6 for applications that require a high gloss, molded in color surface&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | Good surface appearance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 2.0 to 3.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 32.1 | MPa | ASTM D638 |
| yield | 41.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 20 | % | ASTM D638 |
| yield | 10 | % | ASTM D638 |
| Bending modulus | 1310 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 320 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 63 | °C | |
| Drying time | 6.0 to 8.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 241 | °C | |
| Barrel middle temperature | 241 | °C | |
| Barrel front temperature | 241 | °C | |
| Processing (melt) temperature | 232 to 257 | °C | |
| Mold temperature | 52 to 57 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Vent depth | 0.025 to 0.038 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |