Queo™ 7001LA

About
Queo 7001LA is an ethylene based octene-1 elastomer, produced in a solution polymerisation process using a metallocene catalyst. Applications Demonstrated applications include: Low SIT Seal layers in lamination and flexible barrier films Cling film Surface protection film Halogen free flame retardant compounds Noise reduction in e.g. automotive applications High strength flexible films Extrusion coating Additives Queo 7001LA contains a low amount of processing stabilizers. Special Features Queo 7001LA is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. High clarity High flexibility and surface softness Bridging of plastic and elastomeric properties Low peak melting point&&

About

Queo 7001LA is an ethylene based octene-1 elastomer, produced in a solution polymerisation process using a metallocene catalyst. Applications Demonstrated applications include: Low SIT Seal layers in lamination and flexible barrier films Cling film Surface protection film Halogen free flame retardant compounds Noise reduction in e.g. automotive applications High strength flexible films Extrusion coating Additives Queo 7001LA contains a low amount of processing stabilizers. Special Features Queo 7001LA is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. High clarity High flexibility and surface softness Bridging of plastic and elastomeric properties Low peak melting point&&

Product Description
Supplier	Borealis AG
Generic	乙烯基辛烯塑料
Material Status	Commercial: Active
Features	Good Rigidity,Good Clarity,Halogen free,Flame Characteristics,High Flexibility,Octene copolymer,Soft,Low temperature heat sealing
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.870	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	1.0	g/10min	ISO 1133
Mooney viscosity
ML 1+4，100℃	30	MU	DIN 53523

film	Nominal value	Unit	Test method
Initial sealing temperature	< 60.0	℃	Internal Method
Drop hammer impact	> 392.3	kN/m	ISO 7765-1

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	无断裂		ISO 180

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -90.0	℃	ISO 974
Vicat Softening Temp	39.0	℃	ISO 306/A
Melting temperature	56.0	℃	ISO 11357-3

optical performance	Nominal value	Unit	Test method
gloss	> 100		ISO 2813
Haze	< 5.0	%	ASTM D1003

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	74
Shaw’s D	21
tensile strength
fracture	7.00	MPa	ISO 527-2
Tensile strain
fracture	> 400	%	ISO 527-2
Bending modulus	8.00	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.