| About |
|---|
| FS3011E is a homopolymer polypropylene intended for the extrusion of biaxially oriented film. It is easy to process and suitable for high speed BOPP line. The film made from this resin exhibit excellent transparency, excellent mechanical and barrier properties. It is also suitable for metallization. Applications Food packaging Printing lamination Adhesive tape Cigarette packaging Metalized film&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Clarity,Quick molding cycle,Electroplating,Block resin,Homopolymer |
| Availabilitys | Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.898 | g/cm³ | ASTM D792-A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 20 µ m | 2100 | MPa | |
| 1% secant, TD: 20 µ m | 3850 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, fracture, 20 µ m | 100 | MPa | |
| TD, fracture, 20 µ m | 215 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 20 µ m | 85 | % | |
| TD, fracture, 20 µ m | 15 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 2.8 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 153 | ℃ | ASTM D1525 1 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，20 µm | 155 | ASTM D2457 | |
| Haze | |||
| 20 µm | 0.10 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 98 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 32.0 | MPa | |
| fracture | 19.0 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 9.0 | % | |
| fracture | 170 | % | |
| Bending modulus | 1270 | MPa | ASTM D790 |
| bending strength | 35.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |