| EL-LENE L2009F is a butene LLDPE resin with Slip and Antiblocking agent.&& |
| Product Description | |
|---|---|
| Supplier | SCG |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,High impact resistance,High Heat Resistance,Solvent resistance,Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 25% non-ionic surfactant, molded, F50 | > 1000 | hr | ASTM D1693B |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 38 µ m | 260 | MPa | ASTM D882 |
| 2% secant, TD: 38 µ m | 272 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 38 µ m | 11.8 | MPa | ASTM D882 |
| TD, yield, 38 µ m | 13.7 | MPa | ASTM D882 |
| MD, fracture, 38 µ m | 37.3 | MPa | ASTM D882 |
| TD, fracture, 38 µ m | 34.3 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 38 µ m | 1000 | % | ASTM D882 |
| TD, fracture, 38 µ m | 1200 | % | ASTM D882 |
| Drop hammer impact | |||
| 38 µm | 130 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：38 µm | 150 | g | ASTM D1922 |
| TD：38 µm | 370 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 102 | ℃ | ASTM D1525 |
| Melting temperature | 122 | ℃ | ASTM D2117 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 38 µm | 52 | ASTM D2457 | |
| Haze | |||
| 38 µm | 16 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |