| About |
|---|
| Alkatane HD0840 is a very high molecular weight High Density Polyethylene copolymer resin, especially formulated for use in large part mouldings where strength and rigidity are of importance. It combines excellent impact strength with good ESCR. Alkatane HD0840 is especially suited for blow moulding drums from 15L to 220L and supported IBC’s to 1000L in volume. Suitability for use in any application should be determined by appropriate performance testing. For outdoor applications, an appropriate UV stabilization package should be added.&& |
| Product Description | |
|---|---|
| Supplier | Qenos |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,High impact resistance,Food contact compliance,High molecular weight,Copolymer,High ESCR |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.060 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 7.0 | g/10min | ASTM D1238 |
| 190℃，5.0kg | 0.30 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693B | ||
| 10% non-ionic detergent, molded, F50 | 250 | hr | ASTM D1693B |
| 100% non-ionic detergent, molded, F50 | > 1000 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30 ℃, molded | 310 | J/m | ASTM D256-A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 64 | ASTM D2240 | |
| tensile strength | |||
| Yield, molding | 26.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 900 | % | ASTM D638 |
| Bending modulus | |||
| Compression Molding | 960 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 2.0 in/min |
| 3. 0.50 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |