| About |
|---|
| Automotive wheel covers. Offers superior processability/flow and better chemical resistance when exposed to many automotive fluids over PX0844.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Solvent resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 44.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 2000 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 68.3 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 130 | J/m | ASTM D256 |
| 23℃ | 290 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -40℃，Energy at Peak Load | 33.9 | J | ASTM D3763 |
| 23℃，Energy at Peak Load | 39.5 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 113 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 127 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 243 to 293 | °C | |
| Barrel middle temperature | 254 to 299 | °C | |
| Barrel front temperature | 266 to 304 | °C | |
| Nozzle temperature | 277 to 304 | °C | |
| Processing (melt) temperature | 277 to 304 | °C | |
| Mold temperature | 71 to 99 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |