| INSPIRE™ TF1305 ESU 是滑石粉填充，具有高抗冲性能的PP改性树脂。这一规格适用于有较高外观要求，耐刮擦，抗紫外的汽车零部件。由于其极高的抗冲击性，也特别适合要求高延展性的汽车内饰应用。 应用: 仪表板骨架 仪表板饰件 中控台 门板 门板文件袋 内饰件 卡车饰件&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Ductility,low-temperature impact resistance,High scratch resistance |
| Availabilitys | Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.6 | g/10min | ISO 1133 |
| Shrinkage rate | 0.90 to 1.2 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1950 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 25.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 70 | % | ISO 527-2/50 |
| Bending modulus | 1850 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 5.0 | kJ/m² | ISO 180-1A |
| 0℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 25 | kJ/m² | ISO 180-1A |
| Multi axial instrumented impact energy | |||
| 0 ℃, toughness failure | 50.0 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 110 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 58.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 135 | ℃ | ISO 306/A120 |
| Linear coefficient of thermal expansion | |||
| MD | 8.5E-5 | 1/℃ | ASTM D696 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |