| About |
|---|
| Type : Pearlthane® D11H92S is a polycaprolactone copolyester-based thermoplastic polyurethane. Main Application : Injection Moulding Special Features : Excellent flow and mechanical properties and an outstanding low compression set value and high temperature resistance.&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | TPU-Capro |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High liquidity,Quick molding cycle,High Heat Resistance |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 2781 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| 500 mm | 46.0 | MPa | ISO 527-2/5A |
| 100% strain, 500 mm | 10.0 | MPa | ISO 527-2 |
| 300% strain, 500 mm | 21.0 | MPa | ISO 527-2 |
| tear strength | 130 | kN/m | ISO 34-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | ISO 306/A50 | ||
| A50 | 139 | ℃ | ISO 306/A50 |
| A50 | 133 | ℃ | ISO 306/A50 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shore A, 1 second | 92 | ISO 868 | |
| Shore D, 1 second | 46 | ISO 868 | |
| Tensile strain | |||
| Fracture, 500 mm | 460 | % | ISO 527-2/5A |
| abrasion resistance | 20.0 | mm³ | ISO 4649-A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 3.0 | hr | |
| Barrel rear temperature | 190 | °C | |
| Barrel middle temperature | 195 | °C | |
| Barrel front temperature | 195 | °C | |
| Nozzle temperature | 200 | °C | |
| Mold temperature | 40 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 5 |
| 3. Method Ba, Angle (Unnicked) |
| 4. Unannealed |
| 5. Annealed |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |