| About |
|---|
| LNP STAT-KON OE004A is a compound based on PPS (branched) resin containing Carbon Fiber. Added features include: Electrically Conductive. (only Black is UL listed) |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Conductive,Branched polymer structure |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.10 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 21600 | MPa | ISO 527-1-2 |
| Tensile stress (yield) | 185 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.1 | % | ISO 527-2/5 |
| Bending modulus | 15700 | MPa | ISO 178 |
| Bending stress | 242 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 25 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 4.0 mm, 64 mm span | 277 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 256 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| Flow: 23~60 ℃ | 1.1E-5 | 1/℃ | |
| TD：23~60℃ | 5.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 120 to 150 | °C | |
| Drying time | 4.0 | hr | |
| Temperature at the rear of the barrel | 305 to 315 | °C | |
| Temperature in the middle of the barrel | 320 to 330 | °C | |
| Front temperature of material barrel | 330 to 345 | °C | |
| Processing (melt) temperature | 315 to 320 | °C | |
| Mold temperature | 140 to 165 | °C | |
| Back pressure | 0.200 to 0.300 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |