| About |
|---|
| LNP* STAT-LOY* 9X03508 is a compound based on PPO+PA66 resin containing Proprietary Filler(s). Added features of this material include: Antistatic, Flame Retardant, High Impact. Also known as: LNP* STAT-LOY* Compound PDX-03508 Product reorder name: 9X03508&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Active |
| Features | High impact resistance,Flame Characteristics,Antistatic property |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Water absorption rate | |||
| 24hr，50% RH | 0.90 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 4830 | MPa | ASTM D638 |
| — | 4470 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 53.1 | MPa | ASTM D638 |
| yield | 59.0 | MPa | ISO 527-2 |
| fracture | 53.1 | MPa | ASTM D638 |
| fracture | 58.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 2.1 | % | ASTM D638 |
| yield | 2.5 | % | ISO 527-2 |
| fracture | 2.2 | % | ASTM D638 |
| fracture | 2.8 | % | ISO 527-2 |
| Bending modulus | |||
| — | 3450 | MPa | ASTM D790 |
| — | 4000 | MPa | ISO 178 |
| bending strength | |||
| — | 82.7 | MPa | ASTM D790 |
| — | 96.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 37 | J/m | ASTM D256 |
| 23℃ | 4.2 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 430 | J/m | ASTM D4812 |
| 23℃ | 27 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 8.00 | J | ASTM D3763 |
| — | 1.90 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 230 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 218 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 186 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 179 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ASTM E831, ISO 11359-2 | ||
| MD：-40~40℃ | 6.5E-5 | 1/℃ | |
| TD：-40~40℃ | 4.3E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+10 to 1.0E+12 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82.2 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 199 to 210 | °C | |
| Barrel middle temperature | 210 to 221 | °C | |
| Barrel front temperature | 221 to 232 | °C | |
| Processing (melt) temperature | 199 to 232 | °C | |
| Mold temperature | 37.8 to 54.4 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |