| About |
|---|
| Fiberfil® PP-15/T/10/20 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 22% talc. It is available in North America. Primary characteristic: homopolymer.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Homopolymer |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：3.2 mm | 1.0 | % | ASTM D955 |
| MD：6.35 mm | 1.2 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.030 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 27 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 93.3 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 98.9 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2550 | MPa | ASTM D638 |
| tensile strength | |||
| 23℃ | 34.5 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 23 ℃ | 20 | % | ASTM D638 |
| Bending modulus | |||
| Tangent, 23 ℃ | 2340 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 60.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 90 to 95 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 77 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 199 to 210 | °C | |
| Barrel middle temperature | 204 to 227 | °C | |
| Barrel front temperature | 182 to 199 | °C | |
| Nozzle temperature | 182 to 193 | °C | |
| Processing (melt) temperature | 199 to 232 | °C | |
| Mold temperature | 32 to 71 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 0.00 to 0.689 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |