| About |
|---|
| Tisester® PBT 30 GFR IS is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in Africa & Middle East or Europe for injection molding. Important attributes of Tisester® PBT 30 GFR IS are: Flame Rated Heat Stabilizer&& |
| Product Description | |
|---|---|
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.30 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Ash Content | 30 | % | ISO 3451 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 9.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| B120 | 222 | ℃ | ISO 306/B120 |
| Melting temperature | 225 to 230 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| 3.00 mm | 400 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 750 | ℃ | IEC 60695-2-12 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 84 | ISO 868 | |
| tensile strength | ISO 527-2 | ||
| yield | 150 | MPa | ISO 527-2 |
| fracture | 152 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 2.5 | % | ISO 527-2 |
| fracture | 2.7 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Barrel rear temperature | 220 to 250 | °C | |
| Barrel middle temperature | 220 to 250 | °C | |
| Barrel front temperature | 220 to 250 | °C | |
| Nozzle temperature | 225 | °C | |
| Processing (melt) temperature | 220 to 230 | °C | |
| Mold temperature | 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |